HT18是一款优质的以水泥聚合物为原料的高性能自流平水泥材料。HT18采用优质原料及特别研发配方工艺,是一款专门用于大厚度基础填充找平施工的产品,可满足各类型地面铺装施工对基础找平,特别是大厚度找平处理的需要。适用于高负荷建筑空间如:公共空间、商业、医疗、教育、交通枢纽、工业以及民建等各类建筑空间,特别适用于基础较差,
货翻新改造地面找平处理。
HT18 is a high performance self-leveling cement material with high quality cement polymer as raw material. HT18 adopts high quality raw materials and special formulation technology. It is a product specially used for filling and leveling construction of large thickness foundation. It can meet the needs of foundation leveling, especially for large thickness leveling treatment in varnous types of groundpavement construction. t is suitable for high-load building space such as public space, commerce, medical treatment, education,transportation hub, industry and civil construction, especially for poor foundation, or renovation and leveling of ground.
施工方法 Application Instruction
1、将5.4-5.6升冷净水放入干净的容器中。将袋装物（25kg）倒入容器轻快搅拌并混合至浓稠流体状态中并无团块状。
Put 5.5-6 litres of cold clean water into a clean container. Sprinkle in the sack contents (25kg) whilst stirring briskly and mix to a thick- fluid. Lump-free consistency. Use a drill or mixer fitted with a Mixing Paddle. Do not mix too thinly.
2、将混合好的自流平水泥倒在待施工的区域，用齿耙将材料均匀地铺在地面上，所需厚度根据施工需要调整。使用专用放气滚筒消除气泡。Pour the mixture on the area to be applied, spread the material uniformly to Required thickness using toothed rake. It is the next step to remove entranced air by particular roller.
3、20℃干燥时间约24-48小时。干燥后可采用40-60磨砂纸打磨，提高了表面吸收性。较差的空气流动和较低的温度将影响干燥时间。
Drying time at 20℃ is approx 24-48 hours. Abrading using 40-60 grit sanding paper improves both the surface quality and the absorbency. Poor air-flow and lower temperatures will significantly affect drying times.
覆盖率 Coverage
约1.7公斤粉末/毫米/平米
1.7kg powder/mm/㎡
施工厚度 Thickness
可应用于2-30mm厚度施工
applied from 2mm to 30mm
抗压强度 Compressive strength
30Mpa
抗折强度 Tensile bending strength
6Mpa
可施工时间 Working time
约20分钟
about 20mins
保质期 Quality Grarantee Period
在0-40℃库房内储存，保质期为6个月。
6 months if stored in 0-40℃.
注意事项 Notes
本品在运输、储存中应严格防雨防潮，施工温度不低于5℃。
The product should be protected against frost and direct sun light during transporation, storage and application. Application temperature should not be lower than 5℃.